Injection-grade TPE
Products Characterization:
High fluidity. Soft-touch. Overmolding compatibility with TPE/PP/PE cable.
Application:
TPE wire sheaths. Overmolding PP/PE. Stationery. Tool grip. Sporting equipment
TPE injection guidance:
1. Previous drying of the product 2 hours at 80℃
2. Medium injection pressure & speed
3. Typical barrel temperature suggested
| C1 | C2 | C3 | NOZZLE | MOLD |
170-190 ℃ | 180-200 ℃ | 190-210 ℃ | 190-210 ℃ | 30-60 ℃ |
| Technical Data Sheet | Model | ||||
| Material Properties | Test Standard | Test Condition | Unit | 3072F-EHS-1003T | |
| General Characteristics | Material Category | - | - | - | |
| Appearance(light/Semi-matte/Frosted) | - | - | - | ||
| Extrusion/Injection | - | - | - | ||
| Physical Characteristics | Hardness | ISO 48 | 15S | Shore A | 70 |
| Proportion | ISO 1183 | - | g/cm³ | 1.27 | |
| Melt Index | ISO 1133-1:2011 | 190℃/2.16kg | g/10min | 6 | |
| Brittle Temperature | ISO 812 | - | ℃ | ||
| Mechanical Properties | Elongation | ISO37:2017 | 200mm/min | % | 360 |
| Tensile Strength | ISO37:2017 | 200mm/min | Mpa | 48.503 | |
| Tearing Strength | ISO34-1:2015 | 500mm/min | KN/m | ||
| Hot Air Aging | Elongation Retention Rate | ISO37:2017 | - | % | |
| Tensile Strength Retention Rate | ISO37:2017 | - | % | ||
| Electrical Performance | Volume Resistivity | ASTM D257 | - | Ohm-cm | |
| Permittivity | ASTM D150 | - | - | ||
| Combustion Performance | Vertical Burning Test | UL 94 | 3.0/6.0mm | - | |
| Oxygen Index | ASTM D2863 | - | % | ||
| Feature | |||||
· Competitive price · Respond immediately · Strong R&D capability · Excellent after-sales service